Adhesive composition (case a)

ABSTRACT

An adhesive composition consisting essentially of a styrene-butadiene block copolymer, a tackifier, a zinc salt of rosin and a hydrocarbon solvent. In a preferred embodiment the composition also contains a small amount of water.

Adhesive composition based on styrene-butadiene block copolymers have gained wide use acceptance in recent times because of their favorable processing characteristics, high strength without vulcanization, good creep resistance, good adhesion to a wide variety of substrates and good compatibility with a number of resinous materials. Such adhesive compositions find use as construction adhesives, laminating adhesives, contact cements, wall and tile adhesives, and as caulks and sealants. These compositions are frequently offered as a solvent solution at consistencies commensurate with the application needs. The adhesive solutions, however, have apparently one drawback, namely, that they tend to increase in viscosity on storage over a period of time, and, as such their usable life becomes somewhat restricted. Adhesives that have increased in viscosity on storage need the addition of a solvent or solvent mixtures in order to reduce their consistency to the desirable application viscosity. This method, however, creates an adhesive of a lower solids level, which is undesirable. In instances such as in construction where the adhesives are packed in special paper tubes, such increased viscosity will result in an adhesive difficult to extrude. This could result in a joint having insufficient bond strength due to inadequate adhesive wetting. Accordingly, it is desirable to have available adhesive compositions that will remain sufficiently fluid over their useful life.

I have found that the viscosity characteristics of adhesive compositions composed of a styrene-butadiene block copolymer,, a tackifier and a hydrocarbon solvent upon storage over long periods of time can be improved by incorporating therein a zinc salt of rosin, preferably a zinc salt of rosin and a small amount of water.

The styrene-butadiene block copolymer present in the adhesive composition of the present invention has the following general configuration:

    A -- B -- A

wherein each terminal A is a styrene polymer block with a glass transition temperature above about room temperature (26° C.) and which is relatively incompatible with elastomeric segment B, defined hereinafter, with the average molecular weight of each A being from about 5,000 to about 125,000, preferably from about 15,000 to about 100,000. B is butadiene polymer with a glass transition temperature below about room temperature (26° C.) with the average molecular weight of B being from about 15,000 to about 250,000, preferably from about 25,000 to about 150,000. The difference in glass transition temperature between an end block A and a center block B is preferably greater than about 100° C. In the block copolymer used herein the total of the terminal blocks A will amount to about 20 to about 80 weight per cent, preferably from about 23 to about 50 weight per cent, based on the total weight of the block copolymer.

The tackifier used herein can be any of the resinous substances known in the art for enhancing the tack of adhesive compositions, for example, aromatic hydrocarbon resins, at least one of whose components can be derived from petroleum or coal tar distillates. Particularly suitable are those selected from the group consisting of resins based on coumarone or indene, such as coumarone-indene resins, styrene-indene-isoprene terpolymers, etc. By "coumarone-indene resins" I mean to include fusible, low molecular weight polymers obtained through catalytic and/or thermal polymerization of mixtures containing coumarone and indene having Ring and Ball softening temperatures of about 38° to about 165° C. In general, the softening point of the tackifier will be between about 38° to about 160° C., preferably between about 70° and 155° C.

The third component required herein is a hydrocarbon solvent or mixtures thereof boiling between about 50° to about 145° C., preferably between about 55° to about 120° C., at atmospheric pressure. Those boiling below the defined range will be released too rapidly from the adhesive composition, causing handling problems, such as insufficient working time, while those boiling above the defined range may require a longer time than normal time for the adhesive to set. Solvents which can be used are aromatics having from six to eight carbon atoms, such as toluene, the xylenes, etc.; aliphatics having from six to eight carbon atms, such as normal hexane, normal octane, etc., ketones having from two to four carbon atoms, such as methyl ethyl ketone, acetone, etc.; esters having from two to four carbon atoms, such as ethyl acetate, butyl acetate, etc.; etc.

In order to enhance the viscosity, characteristics of an adhesive composition containing the above components upon storage, there is also incorporated therein a controlled amount of a zinc salt of rosin (including a disproportionated rosin) having a zinc content of between about 4 and about 9 weight per cent and a melting point (Ring and Ball softening points) of between about 80° to about 190° C. Rosin disproportionation involves, for example, heating the resin in excess of 200° C. to convert the oxidation-susceptible sites, e.g., conjugated double bond in the abietic acid structure, to less susceptible structures, such as dehydro-abietic acid, tetrahydro-abietic acid and dihydroabietic acid. Still additional improvement is obtained by the further incorporation therein of a controlled amount of water.

The adhesive composition of this invention can be prepared in any conventional manner. For example, the ingredients can be added to the solvent in any order, after which mixing can take place until a substantially homogeneous mixture is obtained. Such mixing can be carried out at room temperature and room pressure over a period of about 1 to about 4 hours or, alternatively, all of the ingredients can be mixed and set aside for about 24 hours, during which dissolution of the various adhesive components takes place.

The adhesive compositions herein will consist essentially of the following components within the following ranges, assuming the presence of 100 parts by weight of the styrene-butadiene component in the final composition.

    ______________________________________                                                    Weight Percent                                                      Component    Broad Range   Preferred Range                                     ______________________________________                                         Styrene-Butadiene                                                               Block Copolymer                                                                             100          100                                                 Tackifier    10-400         20-300                                             Solvent       100-5,000     500-4,000                                          Zinc Salt of Rosin                                                                          0.1-40        0.5-20                                              Water        0-10          0.1-5.0                                             ______________________________________                                    

If desired other components which can impart a desirable characteristic to an adhesive composition but which do not appreciably alter its fundamental nature, can also be incorporated in the composition. Thus, a filler, such as a clay or calcium carbonate in an amount of about 5 to about 40 weight per cent, preferably about 10 to about 30 weight per cent, based on the weight of the final composition, an antioxidant, such as 1,3,5-trimethyl-2,4,6(3,5-ditertiarybutyl-4-hydroxybenzyl) benzene, in an amount of about 0.1 to about 5 weight per cent, preferaably about 0.25 to about 1.5 weight per cent, based on the weight of the final composition, etc., can also be incorporated in the adhesive composition of this invention.

The improved composition of this invention can be further understood by reference to the following:

EXAMPLE I

A solvent solution containing toluene, hexane and acetone in a weight ratio of 1:1:1 was added to Kraton 1101, Cumar LX 509 and Zirex, the mixture was permitted to sit for 24 hours at room temperature and room pressure and then mixed for an additional hour until a homogeneous mixture was obtained. The mixture was held at 26° C. and the viscosity thereof was periodically taken.

EXAMPLE II

The run of Example I was repeated except that a small amount of water was also present in the mixture before the mixture was permitted to stand for 24 hours. A control run similar to this Example II and to Example I was also carried out but in the absence of Zirex and water.

The results obtained are tabulated below in Table I.

                  TABLE I                                                          ______________________________________                                                         Example No.                                                                    Control                                                                               I        II                                             ______________________________________                                         Kraton 1101, Gms. 100      100      100                                        Cumar LX 509, Gms.                                                                               56.25    51.25    51.25                                      Solvent Solution, Gms.                                                                           468.75   468.75   468.75                                     Zirex, Gms.       None     5.0      5.0                                        Water, Gms.       None     None     0.5                                        Solids, Weight Percent                                                                           25       25       25                                         Viscosity, Cps (Brookfield RVF)                                                 No. Three Spindle, 26°C.                                               Three Days        624      645      655                                        One Week          659      706      700                                        Two Weeks         688      750      730                                        Three Weeks       705      785      795                                        Five Weeks        720      885      798                                        Seven Weeks       1020     1200     970                                        Nine Weeks        1605     1700     1225                                       Twelve Weeks      4725     2625     1700                                       Twenty Four Weeks 65,500   31,200   7400                                       Fifty Four Weeks  Gel      Fluid    Very                                                                           Fluid                                      ______________________________________                                    

Referring to the components in the adhesive compositions above, Kraton 1101 is a styrene-butadiene block copolymer made and sold by Shell Chemicals wherein the terminal styrene block has a molecular weight of about 5,000 to about 125,000 and the center butadiene block has a molecular weight of about 15,000 to about 250,000, with the styrene block constituting about 30 per cent by weight of the total block. Cumar LX-509 is a coumarone-indene resin made and sold by Neville Chemicals Company having a melting point of 155° C. Zirex is a zinc resinate containing 8.7 weight per cent zinc having a melting point of 158° to 164° C. and is made by Reichold Chemicals, Inc.

The data in Table I illustrates the uniqueness of the adhesive composition defined and claimed herein. In the Control sample the viscosity of the adhesive composition progressively increased until at the end of 54 weeks the composition had become a gel. The addition of a small amount of a zinc salt of rosin to the adhesive composition resulted in a composition having a viscosity of about one-half the Control at the end of 24 weeks. At the end of 54 weeks the composition was still fluid. The presence of both a zinc salt of rosin and water in Example II resulted in a composition of even lower viscosity at the end of 24 weeks. At the end of 54 weeks the composition was still very fluid.

Obviously, many modifications and variations of the invention, as hereinabove set forth, can be made without departing from the spirit and scope thereof and, therefore, only such limitations should be imposed as are indicated in the appended claims. 

I claim:
 1. An adhesive composition consisting essentially of a styrene-butadiene block copolymer, a coumarone-indene tackifier, a solvent selected from the group consisting of aromatic hydrocarbons having from six to eight carbon atoms, aliphatic hydrocarbons having from six to eight carbon atoms, ketones having from two to four carbon atoms and esters having from two to four carbon atoms, said solvents having a boiling point between about 50° and 145° C., a zinc salt of rosin and, optionally, water wherein the components thereof are present in the following ranges:

    Component         Weight Percent                                               ______________________________________                                         Styrene-Butadiene                                                               Block Copolymer  100                                                          Tackifier         10-400                                                       Solvent           100-5,000                                                    Zinc Salt of Rosin                                                                               0.1-40                                                       Water             0-10.                                                        ______________________________________                                    


2. The composition of claim 1 wherein the components are present in the following ranges:

    Styrene-Butadiene                                                               Block Copolymer  100                                                          Tackifier         20-300                                                       Solvent            500-4,000                                                   Zinc Salt of Rosin                                                                               0.5-20                                                       Water             0.1-5.0.                                                


3. The composition of claim 1 wherein the styrene-butadiene block copolymer has the following general configuration:

    A -- B -- A

wherein A is a styrene polymer block having an average molecular weight of about 5000 to about 125,000 and B is a butadiene polymer block having an average molecular weight of about 15,000 to about 250,000.
 4. The composition of claim 3 wherein the styrene polymer block has an average molecular weight of about 15,000 to about 100,000 and the butadiene polymer block has an average molecular weight of about 25,000 to about 150,000.
 5. The composition of claim 3 wherein the total of the terminal blocks A amount to about 20 to about 80 weight per cent of the block copolymer.
 6. The composition of claim 3 wherein the total of the terminal blocks A amount to about 23 to about 50 weight per cent of the block copolymer. 